Sikagard®-403 W
Sikagard®-403 W is a single component, waterborne modified acrylic resin based intermediate and surface coating, containing an antimicrobial additive.
- Seamless, easy to clean finish
- Good resistance to repeated cleaning regimes using mild detergents and cleaning solutions
- Tough and highly durable
- Good water vapour permeability
- More flexible in comparison to standard acrylic paints, improves resistance to cracking and flaking
- Ultra-low emissions
- Good opacity
- Odourless
- Easy to apply
Usage
- Application on concrete, bricks, cement and gypsum based substrates, metal surfaces, timber, tiles and plastic
- Embedment, intermediate and top coat for internal walls and ceilings
- Suitable for production facilities in the pharmaceutical, medical engineering, food and beverage industry, as well as, hospitals, prisons, healthcare and leisure facilities
Advantages
- Seamless, easy to clean finish
- Good resistance to repeated cleaning regimes using mild detergents and cleaning solutions
- Tough and highly durable
- Good water vapour permeability
- More flexible in comparison to standard acrylic paints, improves resistance to cracking and flaking
- Ultra-low emissions
- Good opacity
- Odourless
- Easy to apply
Packaging
5.0 L = 6.60 kg drums 15.0 L = 19.80 kg drums
Colour
white
pastel colour shades on request
Product Details
ENVIRONMENTAL INFORMATION
Conformity with LEED v2009 IEQc 4.2: Low-Emitting Materials - Paints and Coatings
APPROVALS / STANDARDS
- Eurofins, test report No. 392-2014-0027 0301, VOC emission acc. French Regulations Decret DEVL 11019093D, March 23, 2011 and Decret DEVL 11034675A, February 15, 2016.
- PRA, test report No. 77388-004, gloss, fineness, grind wet scrub resistance and contrast ratio according to EN 13300, September 30, 2014.
- Exova Warrigtonfire, test report No. WF 343711, classification reaction to fire according to EN 13501-1:2007+A1:2009, September 15, 2014.
- IMSL, test report No. 2014/02/011.1A-1, determination of antibacterial activity according to ISO 22196, December 29th 2014.
- IMSL, test report No. 2014/12/009.2A, determination of resistance of surface coatings to mould growth according to BS 3900, Part G6, April 21, 2015
- 4wardtesting, test report No. C2882, water vapour transmission rate and water vapour permeability according to ISO 7783-1:2000 (superseded by EN ISO 7783:2011, November 30, 2011), August 29, 2014.
- Eurofins, test report No. 392-2015-00292201, determination of VOC and SVOC content according ISO 11890-2, CEPE/EC/2015-04-13 and Commission Decision 2014/312/EU, October 6, 2015
- KIWA GmbH Polymer Institute, test report P10108-E, determination of crack bridging properties according to DIN EN 1062-7, April 12, 2016
- Campden BRI Group, test report No. S/REP/139540/1Sensory Evaluation of the Taint Potential, Triangle Test Method TES -S-002, Odour Transfer Method, July 15, 2016
Chemical Base
Styrene-acrylic copolymer dispersion, waterborne
Shelf Life
12 months from date of production
Storage Conditions
Store in closed, sealed and undamaged packaging in dry conditions. Protect from direct sunlight and frost.
Density
~ 1.34 kg/l (+23 °C) | (EN ISO 2811-1) |
Solid Content by Weight
~ 61 %
Solid Content by Volume
~ 47 %
Tensile Strength
~ 2.8 N/mm² unreinforced | (EN ISO 527-3) |
Tensile Adhesion Strength
> 1.5 N/mm² to concrete primed with Sika Bonding Primer | (ISO 4624) |
Chemical Resistance
Resistant to mild detergents and cleaning agents. Please contact Sika technical service for specific information.
Disinfection with Hydrogen Peroxide Vapour:
- Resistant when using Steris VHP technology
- Resistant to PEA vaporisation technology, when a system build up with glass fibre reinforcement is used
- Resistant when using Oxypharm vaporiser type NOCOSPRAY under following conditions:
Disinfectant | Concentration | Setting at vaporiser | Contact time |
NOCOLYSE Mint (6 %) | 1 ml/m³ | 20 m³ (1.5 minutes vaporisation) | 30 min |
NOCOLYSE One Shot (12 %) | 3 ml/m³ (2 cycles) | 45 m³ (5 minutes vaporisation) | 30 min |
NOCOLYSE Food (7.9 %) | 1 ml/m³ | 20 m³ (1.5 minutes vaporisation) | 30 min |
NOCOLYSE Food (7.9 %) | 5 ml/m³ (2 cycles) | 75 m³ (5 minutes vaporisation) | 60 min |
Permeability to Water Vapour
~ 37.5 g/m² in 24 hours | (EN ISO 7783-1) |
Application
Layer Thickness
Wet film thickness | ~ 200 µm per layer unreinforced |
Dry film thickness | ~ 100 µm per layer unreinforced |
Product Temperature
+8 °C min. / +35 °C max.
Ambient Air Temperature
+8 °C min. / +35 °C max.
Relative Air Humidity
< 80 %
Dew Point
Beware of condenstation Substrate temperature must be at least +3 °C above dew point
Substrate Temperature
+8 °C min. / +35 °C max.
Substrate Moisture Content
Visible damp free
Curing Time
Before overcoating with Sikagard®-403 W
Temperature | Minimum | Maximum |
+10 °C | 4 hours | 7 days |
+20 °C | 2 hours | 7 days |
+30 °C | 1 hour | 7 days |
Before overcoating with 2-comonent top coats
Temperature | Minimum | Maximum |
+10 °C | 16 hours | 7 days |
+20 °C | 8 hours | 7 days |
+30 °C | 4 hours | 7 days |
Consumption
~ 0.28 kg/m² per layer unreinforced
~ 0.80 kg/m² per layer for reinforcement with Sika Reemat Premium
APPLICATION
Stir product mechanically until a uniform liquid has been achieved. Use a low speed electrical stirrer (300–400 rpm) to avoid air entrapment. For roller application use short piled roller.
For airless application use tip sizes from 0.38 to 0.53 mm and angle from 40° to 60°.
CLEANING OF TOOLS
Clean all tools with water immediately after use. Hardened and/or cured material can only be removed mechanically.