Sikafloor®-263 SL Décor
Sikafloor®-263 SL Décor System is a self-smoothing epoxy based 3 mm thick screed. It is composed of Sikafloor263 SL resin high performances solvent free epoxy resin mixed with selected quartz sand and coloured special Sikafloor® Décor Granules giving an endless combination of decorative finishes.
- Decorative with endless finish combination achievable
- Good chemical and mechanical resistance
- Easy application
- Economical
- Solvent-free
- Tight, semi glossy surface
- Matt finish possible
Usage
For the production of decorative self-smoothing floors on concrete and cement screeds with normal up to medium heavy wear e.g. storage and assembly halls, laboratories, pharmaceutical industry, canteens, offices, shops etc.Advantages
- Decorative with endless finish combination achievable
- Good chemical and mechanical resistance
- Easy application
- Economical
- Solvent-free
- Tight, semi glossy surface
- Matt finish possible
Packaging
Component A: 12.3 kg/pail Component B: 3.2 kg/pail Component C: 7.8 kg/bag Component D: 3.1 kg/bag Total pack size: 26.4 kg per set
Colour
Component A: Pigmented; liquid Component B: Transparent; liquid Component C: White; quartz sand Component D: White, Black; inert fillers Sikafloor®-263 SL Décor system is available in 6 Standard Colours:
light grey 7035, grey 7032, beige 1001, blue 5012, green 6011, etc.
Product Details
Chemical Base
Component A and B: epoxy Component C: quartz sand Component D: polymer
Shelf Life
12 months from the date of production, if stored properly in original, unopened and undamaged sealed packaging.
Storage Conditions
Store in dry conditions, protect from direct sunlight.
Density
Sikafloor®-263 SL Décor (all component mixture) : ~ 1.6 kg/L All Density values at +23 °C.
Solid Content
Resin: ~ 100 % (by volume) / ~ 100 % (by weight)
Shore D Hardness
| 7 days (+23 °C) | ~ 75 |
Abrasion Resistance
| 22 mg | (CS10 Wheel/1000 g/1000 cycles) |
Compressive Strength
| Resin (Part A+B) : (28 days / +23 °C) | ~ 60 N/mm2 |
Tensile Strength in Flexure
| Resin (Part A+B): (28 days / +23 °C) | ~ 30 N/mm2 |
Tensile Adhesion Strength
| > 1.5 N/mm2 | (failure in concrete) |
Chemical Resistance
Resistant to many chemicals. Please ask for a detailed chemical resistance table.
Thermal Resistance
| Exposure* | Dry heat |
| Permanent | +50 °C |
| Short-term max. 7 d | +80 °C |
| Short-term max. 12 h | +100 °C |
Short-term moist/wet heat* up to +80 °C where exposure is only occasional (steam cleaning etc.) *No simultaneous chemical and mechanical exposure.
Application
Ambient Air Temperature
+18 °C min / +30 °C max
Relative Air Humidity
80 % r.h. max.
Dew Point
Beware of condensation! The substrate and uncured floor must be at least 3 °C above dew point to reduce the risk of condensation or blooming on the floor finish.
Substrate Temperature
+18 °C min. / +30 °C max.
Substrate Moisture Content
≤ 4 % pbw moisture content. Test method: Sika®-Tramex meter or CM-measurement. No rising moisture according to ASTM (Polyethylene-sheet).
Pot Life
| Temperature | Time |
| +20 °C | ~ 25 min |
| +30 °C | ~ 15 min |
Applied Product Ready for Use
| Temperature | Foot trafic | Light trafic | Full cure |
| +25 °C | ~ 24 hours | ~ 3 days | ~ 7 days |
| +35 °C | ~ 16 hours | ~ 2 days | ~ 5 days |
Consumption
| System | Product | Consumption |
| Primer | Sikafloor®-156 | 0.3–0.5 kg/m2 |
| Self-smoothing wearingcourse (Film thickness ~ 3.0 mm ) | Sikafloor®-263 SL Décor (A + B + C + D) | For a 3 mm DFT: 4.8 kg/m2 |
| Matt Sealer (optional) | Sikafloor®-304 W | Refer to PDS of Sikafloor®-304 W |
Levelling (scratch coat) is optional, depending on substrate conditions, but it is necessary to have a good floor flatness to achieve best Sikafloor®-263 SL Décor Systems aesthetic. Use of Sikafloor®-304 W, clear matt sealer is recommended when improved UV stability and scratch resistance are required. (please consult product data sheet) These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level and wastage etc.
MIXING
Prior to mixing, stir part A mechanically. When all of part B has been added to part A, mix continuously for 2 minutes until a uniform mix has been achieved.
When parts A and B have been mixed, Add part C and D and carry out additional mixing for 2 minutes until a uniform consistency has been achieved. To ensure thorough mixing pour materials into another container and mix again to achieve a consistent mix. Over mixing must be avoided to minimise air entrainment.
MIXING TOOLS
Sikafloor®-263 SL Décor must be thoroughly mixed using a low speed stirrer (300–400 rpm) or other suitable equipment.
APPLICATION
Prior to application, confirm substrate moisture content, r.h. and dew point. If > 4 % pbw moisture content, Sikafloor® EpoCem® may be applied as a T.M.B. (temporary moisture barrier) system.
Levelling: Rough surfaces need to be levelled first. Therefore use e.g. Sikafloor®-161 HC levelling mortar (see PDS).
Self-smoothing wearing course: Sikafloor®-263 SL Décor mixture is poured, spread evenly by means of a large surface scraper (preferably with pins rather than teeth). The scrapper is then turned down for gently smoothing the spread material.
Roll immediately in two directions with a spiked roller to ensure even thickness and to remove entrapped air
Matt Sealer Coat (if needed): For areas to be particularly exposed to traffic, light grinding of Sikafloor®-263 SL Décor prior application of Sikafloor®-304 W can be recommended. On a clean, dustfree surface, Sikafloor®-304 W shall then be uniformly spread and apply using short pile nylon roller. Please consult product data sheet for mixing and application details.
CLEANING OF TOOLS
Clean all tools and application equipment with Thinner C immediately after use.Hardened / cured material can only be mechanically removed.
CLEANING
To maintain the appearance of the floor after application, Sikafloor®-263 SL Décor System must have all spillages removed immediately and must be regularly cleaned using rotary brush, mechanical scrubbers, scrubber dryer, high pressure washer, wash and vacuum techniques etc. using suitable detergents and waxes.