Product Data Sheet Show all documents

Sikadur®-30

Thixotropic epoxy adhesive for bonding reinforcement

Sikadur®-30 is a thixotropic, structural 2-component adhesive, based on a combination of epoxy resins and special filler, designed for use at normal temperatures between +8 °C and +35 °C.

Sikadur®-30 has the following advantages:
  • Easy to mix and apply.
  • No primer needed.
  • High creep resistance under permanent load.
  • Very good adhesion to concrete, masonry, stonework, steel, cast iron, aluminium, timber and Sika® CarboDur® Plates.
  • Hardening is not affected by high humidity.
  • High strength adhesive.
  • Thixotropic: non-sag in vertical and overhead applications.
  • Hardens without shrinkage.
  • Different coloured components (for mixing control).
  • High initial and ultimate mechanical resistance.
  • High abrasion and shock resistance.
  • Impermeable to liquids and water vapour.
Product Data Sheet Show all documents

Usage

Adhesive for bonding structural reinforcement, particularly in structural strengthening works. Especially for the following uses:
  • Sika® CarboDur® Plates to concrete, brickwork and timber (for details see the Sika® CarboDur® Product Data Sheet, the “Method Statement for Sika® CarboDur® Externally Bonded Reinforcement” Ref: 850 41 05 and the “Method Statement for Sika® CarboDur® Near Surface Mounted Reinforcement” Ref: 850 41 07).
  • Steel plates to concrete (for details see the relevant Sika Technical information).
 

Advantages

Sikadur®-30 has the following advantages:
  • Easy to mix and apply.
  • No primer needed.
  • High creep resistance under permanent load.
  • Very good adhesion to concrete, masonry, stonework, steel, cast iron, aluminium, timber and Sika® CarboDur® Plates.
  • Hardening is not affected by high humidity.
  • High strength adhesive.
  • Thixotropic: non-sag in vertical and overhead applications.
  • Hardens without shrinkage.
  • Different coloured components (for mixing control).
  • High initial and ultimate mechanical resistance.
  • High abrasion and shock resistance.
  • Impermeable to liquids and water vapour.

Packaging

6 kg (A+B)

Pre-batched unit

pallets of 480 kg (80 x 6 kg)

Not pre-dosed industrial packaging (pallets at 14 pails):

Component A

30 kg pails

Component B

10 kg pails

Colour

Component A : white

Component B : black

Components A+B mixed : light grey

Product Details

Sustainability / Certifications / Approvals

ENVIRONMENTAL INFORMATION

  • Conformity with LEED v4 MRc 4 (Option 2): Building Product Disclosure and Optimization - Material Ingredients
  • Conformity with LEED v2009 IEQc 4.1: Low-Emitting Materials - Adhesives and Sealants

APPROVALS / STANDARDS

  • IBMB, TU Braunschweig, test report No. 1871/0054, 1994: Approval for Sikadur®-30 Epoxy adhesive.
  • IBMB, TU Braunschweig, test report No. 1734/6434, 1995: Testing for Sikadur®-41 Epoxy mortar in combination with Sikadur®-30 Epoxy adhesive for bonding of steel plates.

  • Avis Technique N° 3/16-875 (annule et remplace N° 3/10-669) Sika® CarboDur®, SikaWrap®

  • CIT n°290 18/07/2017 (certificato di idoneità tecnica all'impiego) ; Sika ® CarboDur®, SikaWrap®, Sikadur®

  • Adhesive for structural bonding tested according to EN 1504-4, provided with the CE-mark
 
Product Information

Chemical Base

Epoxy resin

Shelf Life

24 months from date of production

Storage Conditions

Store in original, unopened, sealed and undamaged packaging in dry conditions. Protect from direct sunlight.

Density

1.65 kg/l ± 0.1 kg/l (components A+B mixed) (at +23 °C)

Technical Information

Compressive Strength

Curing Time

Curing Temperature

+10 °C

+35 °C

12 hours

-

~ 85 N/mm2

1 day

~ 55 N/mm2

~ 90 N/mm2

3 days~ 70 N/mm2~ 90 N/mm2
7 days~ 75 N/mm2~ 90 N/mm2

Modulus of Elasticity in Compression

~ 9600 N/mm2 (at 23 °C)

(ASTM D 695)

Tensile Strength

Curing Time

Curing Temperature

+15 °C

+35 °C

1 day

~ 20 N/mm2

~ 26 N/mm2

3 days

~ 23 N/mm2

~ 27 N/mm2

7 days~ 26 N/mm2~ 29 N/mm2

Tensile Adhesion Strength

Curing time

Substrate
Curing temperature
Adhesion strength

7 days

Concrete dry

+23 °C

> 4 N/mm2 *

7 days

Steel

+23 °C

> 21 N/mm2

*100% concrete failure

Shear Strength

Curing time

Curing Temperature

+15 °C

+23 °C

+35 °C

1 day

~ 4 N/mm2

-

~ 17 N/mm2

3 days

~ 15 N/mm2

-

~ 18 N/mm2

7 days~ 16 N/mm2

18 N/mm2 (1)

~ 18 N/mm2

Concrete failure (~ 15 N/mm2)

(1) (DIN EN ISO 4624)

Shrinkage

0.04 %

(FIP: Fédération Internationale de la Précontrainte)

Coefficient of Thermal Expansion

2.5 x 10−5 per °C (Temperature range: −20 °C to +40 °C)

(EN 1770)

Glass Transition Temperature

Curing time

Curing temperature

TG

30 days

+30 °C

+52 °C

Heat Deflection Temperature

Curing time

Curing temperature

HDT

3 hours

+80 °C

+53 °C

6 hours

+60 °C

+53 °C

7 days+35 °C+53 °C
7 days+10 °C+36 °C

Service Temperature

−40 °C to +45 °C (when cured at +23 °C)

Application

Application Information

Mixing Ratio

Component A : Component B = 3 : 1 by weight or volumeWhen using bulk material the exact mixing ratio must be safeguarded by accurately weighing and dosing each component.

Layer Thickness

30 mm max.

Sag Flow

On vertical surfaces it is non-sag up to 3−5 mm thickness at 35 °C

(FIP: Fédération Internationale de la Précontrainte)

Squeezability

4000 mm2 at +15 °C at 15 kg

(FIP: Fédération Internationale de la Précontrainte)

Product Temperature

Sikadur®-30 must be applied at temperatures between +8 °C and +35 °C.

Ambient Air Temperature

+8 °C min. / +35 °C max.

Dew Point

Beware of condensation.Substrate temperature during application must be at least 3 °C above dew point.

Substrate Temperature

+8 °C min. / +35 °C max.

Substrate Moisture Content

Max. 4 % pbwWhen applied to mat damp concrete, brush the adhesive well into the substrate.

Pot Life

Temperature

Potlife

Open time

+8 °C

~ 120 minutes

~ 150 minutes

+20 °C

~ 90 minutes

~ 110 minuets

+35 °C~ 20 minutes~ 50 minutes

The potlife begins when the resin and hardener are mixed. It is shorter at high temperatures and longer at low temperatures. The greater the quantity mixed, the shorter the potlife. To obtain longer workability at high temperatures, the mixed adhesive may be divided into portions. Another method is to chill components A+B before mixing them (not below +5 °C).
Application steps

SUBSTRATE QUALITY

See the Product Data Sheet of Sika® CarboDur® Plates and Sika® CarboDur® BC rods.

SUBSTRATE PREPARATION

See the “Method Statement for Sika® CarboDur® Externally Bonded Reinforcement” Ref: 850 41 05 and the “Method Statement for Sika® CarboDur® Near Surface Mounted Reinforcement” Ref: 850 41 07.

MIXING

Pre-batched units: Mix components A+B together for at least 3 minutes with a mixing spindle attached to a slow speed electric drill (max. 300 rpm) until the material becomes smooth in consistency and a uniform grey colour. Avoid aeration while mixing. Then, pour the whole mix into a clean container and stir again for approx. 1 more minute at low speed to keep air entrapment at a minimum. Mix only that quantity which can be used within its potlife. Bulk packing, not pre-batched: First, stir each component thoroughly. Add the components in the correct proportions into a suitable mixing pail and stir correctly using an electric low speed mixer as above for pre-batched units.

CLEANING OF TOOLS

Clean all tools and application equipment with Sika® Colma Cleaner immediately after use. Hardened / cured material can only be removed mechanically.