Product Data Sheet Show all documents
Sika® Injection-306

Sika® Injection-306

Polyacrylic elastic injection resin for permanent watertight sealing

Sika® Injection-306 is a very low viscous, elastic polyacrylic injection resin with a versatile and adjustable reaction time which can be used in ground water protection zones.

  • Provides a passivating environment for embedded steel reinforcement
  • Adjustable curing time between 10 and 60 minutes
  • Permanently elastic, can absorb limited movement
  • Capable of reversibly absorbing (swelling) and releasing (shrinking) moisture
  • Very low viscosity comparable to water
  • Cured Sika® Injection-306 is insoluble in water and hydrocarbons and resistant to alkalis
Product Data Sheet Show all documents

Usage

  • Crack and joint injection
  • Injection of SikaFuko® injection hoses to seal construction joints
  • Sealing water-bearing cracks and voids
  • Sealing all types of leaking building components in damp or water saturated ground conditions  
  • Sealing leaks where there is some minor movement
  • Sealing drainage pipe joints, that are, or will be, covered with damp or water saturated soil
  • Injection repair of damaged waterproofing membranes (single and double layer systems)
 

Advantages

  • Provides a passivating environment for embedded steel reinforcement
  • Adjustable curing time between 10 and 60 minutes
  • Permanently elastic, can absorb limited movement
  • Capable of reversibly absorbing (swelling) and releasing (shrinking) moisture
  • Very low viscosity comparable to water
  • Cured Sika® Injection-306 is insoluble in water and hydrocarbons and resistant to alkalis

Packaging

Ready to use kit:

Part A (Resin)

2 × 8.0 kg

Accelerator

1 × 1.0 kg

Hardener

4 × 40 g

Measuring cup

1 piece

Additional Accelerator 4 × 1 kg - used for faster reaction times.

Refer to current price list for packaging variations.

Colour

Part A (Resin)

blue - transparent liquid

Accelerator

yellow - transparent liquid

Hardener

white - powder

Product Details

Sustainability / Certifications / Approvals

APPROVALS / STANDARDS

  • Function test with SikaFuko® VT 1,Wissbau,Report No.2002-094-(1A)
  • Function test with SikaFuko® Eco 1,Wissbau,Report No.2002-094-(2A)
  • Mechanical and long time stability test,FH Aachen
  • Compatibility Test with Sikaplan® WP/WT Membranes,MPA,Report No.1200/550/15b
  • Reaction to fire,EN 13501-1,MPA,Report No.K-3159/085/13-MPA BS
Product Information

Chemical Base

3-part polyacylic resin

Shelf Life

12 months from date of production

Storage Conditions

The product must be stored in original, unopened and undamaged sealed packaging in dry conditions. Protect from direct sunlight.

Density

Part A (Resin)

~ 1.07 g/cm3

Accelerator

~ 1.08 g/cm3

Hardener

~ 1.25 g/cm3

Viscosity

~ 3–11 mPa∙s (mixture, at +20 °C)

(acc. ISO 3219)
Technical Information

Reaction to Fire

Class E

Application

Application Information

Mixing Ratio

Table 1

Accelerator Metering Chart

Ambient Temperature and Accelerator quantity (ml)

Reaction time

+5 °C

(+41 °F)

+15 °C

(+59 °F)

+22 °C

(+72 °F)

+30 °C

(+86 °F)

+40 °C

(+104 °F)

10 min

1350*

680*

310

160

20 min

1300 *

340*

230

130

50

30 min

840*

230

140

7030

40 min

640*

160

90

50-

50 min

490

90

60

40-
60 min370603030-

The quantity in Table 1 of accelerator (A1) per 8.0 kg of resin (A), will yield ~ 20 litres of mixed resin. The total accelerator solution must always be 2000 ml (refer to example below).

*Fast reaction – additional accelerator necessary.

Example:
Ambient temperature: +15 °C (+59 °F)
Required reaction time: 30 min

Accelerator = 230 ml
Water = 1770 ml
Total volume = 2000 ml

Note:
1) When using one component pumps: Workability time (pot life) = Factor 0.8 × Reaction time (refer to metering chart)
2) The given data are laboratory parameters and may deviate depending on the situation and conditions on site.

Ambient Air Temperature

+5 °C min. / +40 °C max

Substrate Temperature

+5 °C min. / +40 °C max.

Gel time

10–60 minutes
Consumption

Yield

~ 40 litres per kit
Application steps

MIXING

Mixing Sequence

1. Hardener solution

Pour 10 litres of water in a clean container. Dissolve the content of 2 bags (total 80 g) of hardener powder in the water. Stir with a mixer at low speed the hardener solution thoroughly until Part B is completely dissolved.

2. Accelerator solution

Determine the required quantity of accelerator from the accelerator metering chart (Table 1). Dilute the selected quantity of accelerator with water to a total quantity of 2 litres accelerator solution.

3. Accelerator solution with Part A resin

Pour the 2 litres of accelerator solution into 1 × 8.0 kg container of Part A and shake/mix thoroughly.

4. Resin solution with hardener solution

Depending on the type of injection pump used activate the injection resin using one of the methods below:

  • One component pump: Pour a partial amount of the final pre-mixed solution in the ratio of 1:1 by volume into a clean mixing container. Mix thoroughly and pour into the storage container of the pump.

  • Two component pump: Pour the resin solution into the storage container of the pumps ‘A’ side. Pour the Hardener Solution into the storage container of the pumps ‘B’ side. Then pump at a ratio of 1:1 by volume.

CLEANING OF TOOLS

Clean all tools and application equipment according to the Product Data Sheet for the Sika® Injection Cleaning System.