Product Data Sheet Show all documents
Sikalastic®-8800

Sikalastic®-8800

Polyurea Hot Spray Applied Waterproofing And Protection Membrane (formerly Sikalastic®-841ST)

Sikalastic®-8800 is a 2- part, pure polyurea, hot spray applied, elastic, very fast curing, waterproofing and protection membrane. The fast curing allows an immediate return-to-service time and the spray application allows fast coverage of the substrate.

  • Seamless
  • Very fast reactivity and curing time
  • Almost immediate return-to-service time
  • Fast application
  • Applied by 2-Component hot spray equipment
  • Applicable in temperatures from -20 °C to +50 °C
  • Performs in constant dry temperatures from -30 °C to +100 °C
  • Good crack bridging properties
  • Good chemical and abrasion resistance
  • Not resistant to biogenic sulphuric acid
Talk to Our Experts
Product Data Sheet Show all documents

Usage

Concrete
  • Abrasion resistant protective coating in industrial and manufacturing facilities
  • Waterproofing for cut and cover structures, submersed structures, walkways and balconies, floors and car park decks
  • Water retaining structures in power plants
  • Secondary containment structures
  • Tank, bund and pit lining in sewage and waste water treatment plants
Steel
  • Truck bed lining
  • Waterproofing and wearing layer on steel bridges

Advantages

  • Seamless
  • Very fast reactivity and curing time
  • Almost immediate return-to-service time
  • Fast application
  • Applied by 2-Component hot spray equipment
  • Applicable in temperatures from -20 °C to +50 °C
  • Performs in constant dry temperatures from -30 °C to +100 °C
  • Good crack bridging properties
  • Good chemical and abrasion resistance
  • Not resistant to biogenic sulphuric acid

Packaging

Part A (Isocyanate)

212 kg drums

~189 litres

Part B (Polyamine)

191 kg drums

~189 litres

Refer to current price list for packaging variations.

Colour

Part A

liquid / clear

Part B

liquid / grey

Final finish colour: Standard colour: ~RAL 7012, basalt grey

On request: ~RAL 7004, grey

UV light exposure may lead to yellowing

Product Details

Sustainability / Certifications / Approvals

ENVIRONMENTAL INFORMATION

  • Conformity with LEED v4 MRc 2 (Option 1): Building Product Disclosure and Optimization – Environmental Product Declarations
  • Conformity with LEED v2009 IEQc 4.2: Low-Emitting Materials - Paints and Coatings
  • Sikalastic®-8800 is listed on the Eco-Product Directory as environmentally friendly product choice for green building initiatives. (application no.: PL-01570-2023)

APPROVALS / STANDARDS

  • CE Marking and Declaration of Performance to EN 1504-2 - Surface protection product for concrete - Coating
  • Coating System DIN V 18026, Sikalastic-8800, kiwa, Report No P 9278-1-E
  • Durability test ISO 13438, Sikalastic®-8800, Geoscope, Report No. 131303A
  • Migration test Sikalastic®-8800, eurofins, Report No. G23435_Ver2/BJ1
  • Root resistance DIN 4062, Sikalastic®-8800, kiwa, Report No. P 8395
  • SIKA LIQUID APPLIED WATERPROOFING SYSTEMS Sikalastic®-8800, BBA, Certificate No. 19/5621, Part 1, Part 2
  • Crack-bridging test EN 1062-7, Sikafloor®-156 / Sikalastic®-8800, kiwa, Report No. P 8331a-E
  • Liquid Plastics for Waterproofing in Buildings Part 2, Sikalastic®-8800, kiwa, Report No. P 10064-2-E

  • Radon diffusion coefficient EN ISO/IEC17025, Sikalastic®-8800, CTU in Prague, Test report No. 124042/2017

  • Biological Resistance EN 12225, Sikalastic®-8800, kiwa, Report No. 1.1/26341/0362.0.1.1-2016e
  • Radon test ISO 11665-10, Sikalastic®-8800, IHK Bonn/Rhein-Sieg, Report No. 2016100701e
 
Product Information

Product Declaration

EN 1504-2: Surface protection product for concrete - Coating

Chemical Base

Pure polyurea

Shelf Life

Part A and Part B: 12 months from date of production

Storage Conditions

The product must be stored in original, unopened and undamaged packaging in dry conditions at temperatures between +5 °C and +30 °C. Always refer to packaging.

Density

Part A

~1.12 kg/l

Part B

~1.01 kg/l

Values at +20 °C

Viscosity

Temperature

Part A

Part B

+20 °C

900–1300 mPa·s

600–850 mPa·s

+25 °C

~750 mPa·s

~500 mPa·s
Technical Information

Shore A Hardness

> 50

(DIN 53505)

Mechanical Resistance

0 mgCS17/ 1000 g/ 1000 cy

1.114 mg

H22 / 1000 g / 1000 cy

Tensile Strength

> 20 N/mm²

(DIN 53504)

Crack Bridging Ability

Class A5

Static

Class B4,2

Dynamic

Thermal Resistance

Performs in constant dry temperatures from -30 °C to +100 °C

Permeability to Water Vapour

Sd value H2O ~6.6m

(EN ISO 7783-2)

Permeability to Carbon Dioxide

Sd value CO2 ~201m

(EN 1062-76)

Chemical Resistance

Resistant to many chemicals. Contact Sika Technical Services for additional information.

Application

Application Information

Mixing Ratio

Part A : Part B = 1 : 1 (by volume)

Layer Thickness

> 2mm

Product Temperature

> +65 °C

Ambient Air Temperature

-20 °C min. / +40 °C max.

Relative Air Humidity

< 85 %

Dew Point

Beware of condensation.
The substrate and uncured applied floor material must be at least +3 °C above dew point to reduce the risk of condensation or blooming on the floor finish.

Substrate Temperature

-20 °C min. / +50 °C max.

Curing Time

Final cure ~24 hours at +20 °C

Time is approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.

Gel time

~11 seconds  at + 20 °C

Waiting Time / Overcoating

1–2 minutes at +20 °C
Consumption

Consumption

~1.05 kg / m2 / mm
Application steps

APPLICATION INSTRUCTIONS

Coating System for concrete structure

ProductConsumption

Primer

1 × Sikafloor®-156

0.3-0.5 kg/m²

Broadcast

Light broadcast with quartz sand, 0.3-0.8 mm

1.0-1.5 kg/m²

Base Coat

1 × Sikalastic®-8800

~1.05 kg/m²/mm

Top Coat

1 × Sikalastic® Eau Top or

1 × Sikalastic®-701

~ 0.2 kg/m²
 

~ 0.35 kg/m²

Sikalastic 702® is able to patch repair Sikalastic 8800® and be installed at area that cannot be reached by Sikalastic 8800®. For details please refer to Sikalastic 702® product data sheet.

MIXING

Note: Both components must be heated up to +70 °C. The accuracy of mixing and dosage must be controlled regularly with the spray equipment. Thoroughly stir part B (Amine) using a drum stirrer until a uniform consistent colour is obtained.

APPLICATION

Strictly follow installation procedures as defined in method statements, application manuals and working instructions which must always be adjusted to the actual site conditions.

Prior to application, confirm substrate moisture content, relative air humidity, dew point, substrate, air and product temperatures.

Reference must be made to the Sika Method Statement: Sikalastic®-8800.

CLEANING OF TOOLS

Clean all tools with Thinner C or Sika® Remover-208  immediately after use. The application equipment must cleaned and filled with Mesamoll. Hardened material can only be removed mechanically.